Effect of ZnO/Na 2O (mol) on the Properties of cBN Vitrified Bond Grinding Wheel
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
    摘要:

    通过DSC -TG综合热分析、X衍射分析、线膨胀测试仪、扫描电镜等测试方法研究了ZnO/Na 2 O(mol)( Z 值)对Li 2 O -K 2 O -SiO 2 -Al 2 O 3 -B 2 O 3 系陶瓷结合剂及立方氮化硼砂轮性能的影响,结果发现:ZnO能够抑制α -石英晶相析出,诱导析出低膨胀晶体Li 2 OAl 2 O 3 7.5SiO 2 ,并随着 Z 值的增加,α -石英减少,Li 2 OAl 2 O 3 7.5SiO 2 晶体逐渐增多, Li 2 OAl 2 O 3 7.5SiO 2 晶型结构趋于完整,晶粒尺寸减小,结构更加致密;当砂轮配方一定时,砂轮的体积密度、抗弯曲强度、洛氏硬度均随着 Z 值的增加而增大,气孔率减小,磨削(干磨)铸铁(QT400)时磨耗比先增加后减小;当 Z =0.75时,结合剂的膨胀系数为6.902 9×10 -6 K - 1 ,耐火度为805 ℃,砂轮的烧结温度为845 ℃,抗弯曲强度为73.97 MPa,气孔率为15.65%,磨耗比最大为156.42%.

    Abstract:

    The effect of ZnO/Na 2O molar ratio( Z )on the properties of Li 2O -K 2O -SiO 2 -Al 2O 3 -B 2O 3 system vitrified bonds and cBN grinding wheels were studied with TG -DSC, X -ray diffraction analysis, scanning electron microscopy and thermal expansion coefficient tests. The results showed that the lower inflation crystalline phase(Li 2OAl 2O 37.5 SiO 2)appeared in the vitrified bond. And by increasing the ratio of Z , all the vitrified bonds' topographic crystal temperature, softening temperature, crystal quantity and density increased while the crystal size was reduced. When the wheel formula was fixed, the porosity of wheel decreased by increasing the ratio of Z while the bulk density, hardness and bending strength all increased. But G -ratio(dry -rubbing QT400)increased at the beginning, and then became lower. When the ratio of Z was 0.75, the values of vitrified bonds' expansion coefficient and softening temperature were 6.902 9×10 -6 K -1 and 805 ℃, respectively. Meanwhile, the bending strength, the porosity and G -ratio of cBN grinding wheel were 73.97 MPa,15.65% and 156.42%, respectively.

    参考文献
    相似文献
    引证文献
文章指标
  • PDF下载次数:
  • HTML阅读次数:
  • 摘要点击次数:
  • 引用次数:
引用本文

万 隆 ,翟浩冲,胡伟达,刘小磐,张国威,王志起. ZnO/Na 2 O(mol)对cBN陶瓷砂轮性能的影响[J].湖南大学学报:自然科学版,2011,38(9):64~69

复制
历史
  • 收稿日期:
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期:
  • 出版日期:
作者稿件一经被我刊录用,如无特别声明,即视作同意授予我刊论文整体的全部复制传播的权利,包括但不限于复制权、发行权、信息网络传播权、广播权、表演权、翻译权、汇编权、改编权等著作使用权转让给我刊,我刊有权根据工作需要,允许合作的数据库、新媒体平台及其他数字平台进行数字传播和国际传播等。特此声明。
关闭