Mechanisms for the Enhanced Ceramics Gypsum Modelwith Ordinary Portland Cement
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
    摘要:

    研究了硅酸盐水泥(OPC)对陶瓷模具石膏凝结时间、机械强度及工作性能(吸水性、耐水性、耐溶蚀及耐磨性)的影响,采用XRD,DSC-TG和SEM-EDS测试技术对其作用机理进行深入分析.结果表明:OPC的掺入减少了相同流动度下拌合水量,促进了半水石膏的凝结硬化并使半水石膏硬化体后期强度显著增加,且耐水、耐溶蚀及耐磨性能大幅提高.XRD和SEM-EDS分析表明半水石膏-硅酸盐水泥复合体系主要水化产物有针棒状二水石膏(DH)晶体,细针尖状钙矾石(AFt)晶体及无定形C-S-H凝胶.DH与AFt晶体相互交织生长形成网状结构,C-S-H凝胶填充在晶间孔隙内并覆盖于DH晶体表面使晶胶结构更趋密实,结晶接触点减少,硬化体孔隙率降低、孔径细化,强度、耐水、耐溶蚀性能显著提高;DSC-TG分析得出石膏脱水温度由140 ℃升至150 ℃,表明密实的晶胶结构增强了石膏硬化体热稳定性能.

    Abstract:

    The effects of ordinary Portland cement (OPC) on setting time, mechanical behaviors and working performances, including water absorption, softness efficiency, corrosion-resistance and arasion-resistance of ceramic gypsum model, were investigated. The mechanisms were characterized with the measurements of X-ray diffraction, scanning electron microscopy (SEM) and DSC/TG. The results showed that the amount of water demand was reduced and the setting time was shortened by adding OPC. Besides, the strength at the later stage of hydration was significantly increased by the amount of OPC rising which remarkably enhanced the performances of corrosion-resistance, softness efficiency and arasion-resistance. The mechanisms indicated that CaSO4·2H2O(DH), AFt and C-S-H gel were the main hydration production. The interconnection between needle, clavuligerus DH and acicular AFt crystals together with the filling of C-S-H into pore space led to a more compacted crystal-gel microstructure, which enhanced the macro-performances of gypsum hardened paste. In addition, DTA-TG results indicated that the dehydration temperature of DH was also improved from 140 ℃ to 150 ℃ due to the more compact microstructure of gypsum hardened paste. What's more, the morphology of gypsume was modified to be grainy, noodles-shape and stumpy.

    参考文献
    相似文献
    引证文献
文章指标
  • PDF下载次数:
  • HTML阅读次数:
  • 摘要点击次数:
  • 引用次数:
引用本文

赵敏 ,彭家惠,张明涛,李志新 ,赵海鑫.硅酸盐水泥增强陶瓷模具石膏机理研究[J].湖南大学学报:自然科学版,2014,41(12):46~52

复制
历史
  • 收稿日期:
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2015-01-05
  • 出版日期:
作者稿件一经被我刊录用,如无特别声明,即视作同意授予我刊论文整体的全部复制传播的权利,包括但不限于复制权、发行权、信息网络传播权、广播权、表演权、翻译权、汇编权、改编权等著作使用权转让给我刊,我刊有权根据工作需要,允许合作的数据库、新媒体平台及其他数字平台进行数字传播和国际传播等。特此声明。
关闭