Performance Research of Nano Montmorillonite and Palygorskite Composite Phenolic Resin as the Matrix of Friction Material
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
    摘要:

    在苯酚预聚物中分别添加其质量分数为1.5%的纳米蒙脱石(M)和坡缕石(P),原位聚合了2种酚醛树脂(分别记为PF/M和PF/P).用热分析仪对其进行了TG分析.将合成的PF/M和PF/P为基体分别制备半金属摩擦材料,按照GB5763—2008在XD-MSM定速式摩擦磨损试验机上进行摩擦学性能测试.结果表明:纳米粒子份数为1.5% PF/M的耐热性及其摩擦材料的摩擦学性能均明显优于未有纳米粒子复合的PF和PF/P,在600 ℃时PF/M残炭率较PF/P高4%,较PF高12%,所制备的摩擦材料试样的抗热衰退温度较PF/P和PF树脂摩擦材料分别提高约50 ℃和100 ℃,且摩擦因数稳定,350 ℃高温时段的磨损率较FP-1.5和F-0.0分别降低16.8%和27%.

    Abstract:

    1.5% of the nano montmorillonite (M) and palygorskite (P) were separately added to the phenol prepolymer, and phenolic resins were synthesized in in-situ method (called PF/M and PF/P). The TG analysis of the synthetic resins was carried out. The synthetic resins PF/M and PF/P were used as the new resin matrix to prepare semimetal friction material samples. Tribological performance test was carried on an XD-MSM fixed speed type friction-wear the testing machine. The results show that the heat resistance of PF/M by nano-particles for 1.5% and its tribological performance of friction material are better than no nanoparticle composite PF and PF/P. The carbon residue rate of mass fraction of 1.5% synthetic resin PF/M is more than PF/P and PF, separately increased by 4% and 12% at 600 ℃. The temperature thermal recession of the sample prepared by PF/M is increased by 50 ℃ and 100 ℃ more than the sample prepared by PF/P and no nano-particles composite resin, and has stable friction coefficient. Its wear rate is separately reduced by 16.8% and 27% than FP-1.5 and F-0.0 at the high temperature of 350 ℃.

    参考文献
    相似文献
    引证文献
文章指标
  • PDF下载次数:
  • HTML阅读次数:
  • 摘要点击次数:
  • 引用次数:
引用本文

蔡家斌,周元康,聂华伟,曹阳.纳米蒙脱石和坡缕石复合PF基摩擦材料性能[J].湖南大学学报:自然科学版,2015,42(10):72~77

复制
历史
  • 收稿日期:
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2015-10-29
  • 出版日期:
作者稿件一经被我刊录用,如无特别声明,即视作同意授予我刊论文整体的全部复制传播的权利,包括但不限于复制权、发行权、信息网络传播权、广播权、表演权、翻译权、汇编权、改编权等著作使用权转让给我刊,我刊有权根据工作需要,允许合作的数据库、新媒体平台及其他数字平台进行数字传播和国际传播等。特此声明。
关闭