轧制方式对镁合金生体腐蚀行为的影响
DOI:
作者:
作者单位:

作者简介:

通讯作者:

基金项目:


Effects of Rolling Mode on Bio-corrosion Behavior of Magnesium Alloys
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
    摘要:

    采用光学显微镜、扫描电镜、浸泡质量损失和拉伸测试等手段研究了轧制方式(常规轧制和一道次高应变速率轧制)对镁合金(纯镁, Mg-4Zn, Mg-4Zn-0.3Ca和ZK60)在Hank’s溶液中腐蚀行为的影响.结果表明:与常规轧制态相比,高应变速率轧制态镁合金在长时间浸泡过程中平均腐蚀速率较低,抗拉强度下降幅度较小,耐腐蚀性能明显提高,可归因于晶粒细化、再结晶程度较高、孪晶较少和残余第二相相对粗大等;轧制态合金中第二相较少且较细小,表现为相对均匀的丝状腐蚀.

    Abstract:

    The effects of rolling mode (conventional rolling and high strain-rate rolling in a single pass) on bio-corrosion behavior of magnesium alloys (ZK60, Mg-4Zn-0.3Ca, Mg-4Zn and pure Mg) were investigated by optical microscope (OM), scanning electron microscope (SEM), mass loss of immersion testing and tensile testing. The results showed that magnesium alloy prepared by high strain-rate rolling exhibited lower average corrosion rate and reduced slightly in ultimate tensile strength, compared with the counterpart prepared by conventional rolling. Meanwhile, better corrosion resistance was also exhibited, which could be attributed to the grain refinement, higher DRX extent, fewer twins, and relatively coarse remained second phases. The as-rolled alloys also exhibited a uniform filiform corrosion due to the lower fraction and finer size of the second phase.

    参考文献
    相似文献
    引证文献
文章指标
  • PDF下载次数:
  • HTML阅读次数:
  • 摘要点击次数:
  • 引用次数:
引用本文

陈吉华, 陈冠清, 严红革, 苏斌, 巩晓乐.轧制方式对镁合金生体腐蚀行为的影响[J].湖南大学学报:自然科学版,2016,43(12):24~30

复制
历史
  • 收稿日期:
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2016-12-27
  • 出版日期:
作者稿件一经被我刊录用,如无特别声明,即视作同意授予我刊论文整体的全部复制传播的权利,包括但不限于复制权、发行权、信息网络传播权、广播权、表演权、翻译权、汇编权、改编权等著作使用权转让给我刊,我刊有权根据工作需要,允许合作的数据库、新媒体平台及其他数字平台进行数字传播和国际传播等。特此声明。
关闭