MgSO4 Attack of Cement Based Materials under Electrical Field
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
    摘要:

    已有研究表明电场能够加速水泥基材料硫酸盐侵蚀并可用于快速评价水泥基材料的抗硫酸盐侵蚀性能,但以上研究均是针对电场作用下Na2SO4溶液的侵蚀,鲜有研究电场作用下MgSO4溶液侵蚀行为.本文利用抗蚀系数反映电场对水泥基材料MgSO4侵蚀程度影响,利用XRD和SEM/EDS分析电场作用下水泥基材料的MgSO4侵蚀机理.研究表明:电场加速了水泥基材料MgSO4侵蚀破坏;在电场作用下SO42-离子从阴极进入试件内部,首先与Ca(OH)2反应生成石膏,生成的石膏继续与C3A的水化产物反应生成钙矾石,当C3A的水化产物反应完毕,从外界进入的SO42-离子继续与Ca(OH)2反应生成石膏,其侵蚀产物以石膏为主,其次是钙矾石.

    Abstract:

    Existing studies have shown that electrical field accelerates the sulfate attack, and thus it can be used to rapidly evaluate the sulfate resistance of cement based materials. However, Na2SO4 was mainly used as the corrosion medium in these studies and there were fewer researches on MgSO4 as attack solution under electrical field. Therefore, in this paper, the mechanism of magnesium sulfate attack under electric field was analyzed by means of corrosion resistance coefficient, X ray diffraction (XRD) and Scanning Electron Microscope (SEM) equipped with Energy Dispersive Spectrometer (EDS). The results showed that sulfate ions migrated into the specimens under the action of electrical field and reacted with portlandite to produce gypsum, which reacted further with the hydration products of C3A to form ettringite. After the hydration products of C3A were consumed, the penetrated sulfate ions continued to react with portlandite. As a result, the main attack product was gypsum, followed by ettringite.

    参考文献
    相似文献
    引证文献
文章指标
  • PDF下载次数:
  • HTML阅读次数:
  • 摘要点击次数:
  • 引用次数:
引用本文

罗遥凌,殷吉强,王冲,方正.电场作用下水泥基材料的MgSO4侵蚀[J].湖南大学学报:自然科学版,2017,44(6):69~74

复制
历史
  • 收稿日期:
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2017-07-07
  • 出版日期:
作者稿件一经被我刊录用,如无特别声明,即视作同意授予我刊论文整体的全部复制传播的权利,包括但不限于复制权、发行权、信息网络传播权、广播权、表演权、翻译权、汇编权、改编权等著作使用权转让给我刊,我刊有权根据工作需要,允许合作的数据库、新媒体平台及其他数字平台进行数字传播和国际传播等。特此声明。
关闭