矿渣-水泥-膨润土剪切模量龄期效应 及其影响因素的试验研究
DOI:
作者:
作者单位:

作者简介:

通讯作者:

基金项目:


Experimental Study on Age Effect and Influence Factors of Slag-cement-bentonite's Shear Modulus
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
    摘要:

    采用压电陶瓷弯曲元测试矿渣-水泥-膨润土(S-CB)试样剪切波速的方法,研究了复合胶凝材料含量、矿渣替代率、龄期对S-CB的剪切波速(Vs)与剪切模量(G0)的影响规律. 试验结果表明,S-CB的Vs随龄期的增长、矿渣替代率的减小、复合胶凝材料含量的增大而增大;试验中,S-CB的Vs明显低于同龄期水泥土的Vs,这主要归因于S-CB含水量显著高于水泥土;发现S-CB的硬化发展规律与矿渣替代率紧密相关,与复合胶凝材料含量相关性不明显,基于试验结果提出了矿渣-水泥-膨润土的剪切模量随龄期的预测公式,若测试获得某一复合胶凝材料含量的矿渣-水泥-膨润土的归一公式,可推测相同矿渣替代率的其他复合胶凝材料含量的矿渣-水泥-膨润土的剪切模量.

    Abstract:

    The shear wave velocity of slag-cement-bentonite (S-CB) samples by piezoelectric bending element was tested to study the influence of cementitious material content,slag substitution rate and age on shear wave velocity (Vs) and shear modulus (G0). The test results showed that, with the increase of age, decrease of slag substitution rate and increase of content of cementitious material, shear wave velocity (Vs) of S-CB increased. In the tests, Vs of S-CB is significantly lower than that of cemented clay at the same age. This is mainly due to the higher water content of S-CB than cemented clay. It is observed that the development tendency of S-CB is closely related to the slag substitution rate of cementitious material, and it is not obviously correlated with the content of cementitious material. Based on the test results, the prediction formula for shear modulus of cement-bentonite with age was proposed. If the normalized formula of S-CB with one kind of cementitious material content is obtained by test, the shear modulus of S-CB with other composite cementitious materials content and the same slag replacement rate can be speculated.

    参考文献
    相似文献
    引证文献
文章指标
  • PDF下载次数:
  • HTML阅读次数:
  • 摘要点击次数:
  • 引用次数:
引用本文

李育超,杨佳林,兰吉武,黄根清.矿渣-水泥-膨润土剪切模量龄期效应 及其影响因素的试验研究[J].湖南大学学报:自然科学版,2019,46(9):133~140

复制
历史
  • 收稿日期:
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2019-09-27
  • 出版日期:
作者稿件一经被我刊录用,如无特别声明,即视作同意授予我刊论文整体的全部复制传播的权利,包括但不限于复制权、发行权、信息网络传播权、广播权、表演权、翻译权、汇编权、改编权等著作使用权转让给我刊,我刊有权根据工作需要,允许合作的数据库、新媒体平台及其他数字平台进行数字传播和国际传播等。特此声明。
关闭